Discrete dislocation plasticity analysis of the wedge indentation of films

D. S. Balint, V. S. Deshpande*, A. Needleman, E. Van der Giessen

*Bijbehorende auteur voor dit werk

OnderzoeksoutputAcademicpeer review

82 Citaten (Scopus)
387 Downloads (Pure)

Samenvatting

The plane strain indentation of single crystal films on a rigid substrate by a rigid wedge indenter is analyzed using discrete dislocation plasticity. The crystals have three slip systems at +/- 35.3 degrees and 90 degrees with respect to the indentation direction. The analyses are carried out for three values of the film thickness, 2, 10 and 50 mu m, and with the dislocations all of edge character modeled as line singularities in a linear elastic material. The lattice resistance to dislocation motion, dislocation nucleation, dislocation interaction with obstacles and dislocation annihilation are incorporated through a set of constitutive rules. Over the range of indentation depths considered, the indentation pressure for the 10 and 50 mu m thick films decreases with increasing contact size and attains a contact size-independent value for contact lengths A > 4 mu m. On the other hand, for the 2 mu m films, the indentation pressure first decreases with increasing contact size and subsequently increases as the plastic zone reaches the rigid substrate. For the 10 and 50 mu m thick films sink-in occurs around the indenter, while pile-up occurs in the 2 mu m film when the plastic zone reaches the substrate. Comparisons are made with predictions obtained from other formulations: (i) the contact size-independent indentation pressure is compared with that given by continuum crystal plasticity; (ii) the scaling of the indentation pressure with indentation depth is compared with the relation proposed by Nix and Gao, [1998. Indentation size effects in crystalline materials: a law for strain gradient plasticity. J. Mech. Phys. Solids 43, 411-423]; and (iii) the computed contact area is compared with that obtained from the estimation procedure of Oliver and Pharr [1992. An improved technique for determining hardness and elastic-modulus using load and displacement sensing indentation experiments, J. Mater. Res. 7, 1564-1583]. (c) 2006 Elsevier Ltd. All rights reserved.

Originele taal-2English
Pagina's (van-tot)2281-2303
Aantal pagina's23
TijdschriftJournal of the Mechanics and Physics of Solids
Volume54
Nummer van het tijdschrift11
DOI's
StatusPublished - nov.-2006

Citeer dit