Ductile shear failure of hulk amorphous metallic alloys was studied using a fractographic is analysis. Although the mechanisms of shear deformation and fracture are appeared the same as in conventional amorphous ribbons, some new fractographic features are observed in bulk alloys. Geometric conditions during the nucleation, growth and coalescence of voids result, in some morphological differences.