In Situ Silica Nanoparticle Formation in a Rubber Matrix Monitored via Real-Time SAXS and Solid-State NMR Spectroscopy

Elena Miloskovska*, Michael Ryan Hansen, Cornelius Friedrich, Denka Hristova-Bogaerds, Martin van Duin, Gijsbertus de With

*Bijbehorende auteur voor dit werk

OnderzoeksoutputAcademicpeer review

17 Citaten (Scopus)


Silica formation in a rubber matrix is studied. The hypothesis that the formation proceeds via inverse micelles where the hexylamine present, being a catalyst, also behaves as a surfactant, is made highly plausible. As well-known, the conversion of TEOS into a solid silica particles proceeds via hydrolysis and condensation reactions. These transformations of TEOS comprise consequential substitution of the hydroxyl (-OH) groups with siloxane ones (-OSi), labeled as Q(1): one -OSi group; Q(2): two -OSi groups; Q(3): three -OSi groups; and Q(4): four -OSi groups. Here the kinetics of the sol gel reaction in the rubber matrix was studied as a function of the reaction temperature (40-120 degrees C) by H-1 high-resolution magic-angle spinning (HR-MAS) NMR spectroscopy. Real-time small-angle X-ray scattering (SAXS) measurements of the sol-gel reaction in NR and EPDM rubber matrices were performed in a time scale of 1 s to 60 min with images being acquired every 15 s. The sol-gel reaction in NR and EPDM rubber at 100 degrees C shows an initial fast increase in particle size that decreases gradually for longer reaction times, eventually reaching a plateau where the particle size does not change anymore. In the NR matrix the initial fast increase in particle size lasts approximately 25 min after which the plateau begins, while for the EPDM the initial phase is approximately 50 min. Moreover quantitative Si-29 MAS NMR measurements used for mapping the silicon atoms showed no significant difference in the structure of the silica particles formed after 15 and 60 min reaction time at 100 degrees C, indicating that a good quality silica with a ratio Q(4):Q(3) congruent to 2 can be realized in a relatively short reaction time, thereby offering options for future industrial applications such as reactive extrusion processes.

Originele taal-2English
Pagina's (van-tot)5174-5185
Aantal pagina's12
Nummer van het tijdschrift15
StatusPublished - 12-aug-2014
Extern gepubliceerdJa

Citeer dit