Rheological and Self-Healing Behavior of Hydrogels Synthesized from l-Lysine-Functionalized Alginate Dialdehyde

Arlina Prima Putri, Ranjita K. Bose, Mochamad Chalid, Francesco Picchioni*

*Bijbehorende auteur voor dit werk

OnderzoeksoutputAcademicpeer review

4 Citaten (Scopus)
56 Downloads (Pure)

Samenvatting

Alginate dialdehyde and l-lysine-functionalized alginate dialdehyde were prepared to provide active aldehyde and l-lysine sites along the alginate backbone, respectively. Different concentrations of substrates and the reduction agent were added, and their influence on the degree of l-lysine substitution was evaluated. An amination reduction reaction (with l-lysine) was conducted on alginate dialdehyde with a 31% degree of oxidation. The NMR confirmed the presence of l-lysine functionality with the degree of substitution of 20%. The structural change of the polymer was observed via FTIR spectroscopy, confirming the formation of Schiff base covalent linkage after the crosslinking. The additional l-lysine sites on functionalized alginate dialdehyde provide more crosslinking sites on the hydrogel, which leads to a higher modulus storage rate than in the original alginate dialdehyde. This results in dynamic covalent bonds, which are attributed to the alginate derivative–gelatin hydrogels with shear-thinning and self-healing properties. The results suggested that the concentration and stoichiometric ratio of alginate dialdehyde, l-lysine-functionalized alginate dialdehyde, and gelatin play a fundamental role in the hydrogel’s mechanical properties.

Originele taal-2English
Artikelnummer1010
Aantal pagina's15
TijdschriftPolymers
Volume15
Nummer van het tijdschrift4
DOI's
StatusPublished - feb.-2023

Vingerafdruk

Duik in de onderzoeksthema's van 'Rheological and Self-Healing Behavior of Hydrogels Synthesized from l-Lysine-Functionalized Alginate Dialdehyde'. Samen vormen ze een unieke vingerafdruk.

Citeer dit