Size Effect in Plastic Deformation and Failure of Metallic Glasses

Jozef Miškuf, Kornel Csach, Alena Juríková, Mária Demčáková, Mária Demčáková, Václav Ocelík

OnderzoeksoutputAcademicpeer review

Samenvatting

Depending on the composition and structure of metallic glasses cells with the dimensions in the range from tenths nanometers to tenths micrometers were observed on the ductile fracture surface. The variation in dimple size was compared with the serrations presented on the loading curve at the nanoindentation of the metallic glasses with different compositions. Higher instantaneous deformation can be connected with simultaneous shearing at more suitable shear band configurations. The cell morphology with the various cell sizes is observed at the failure of the metallic glasses. At the failure of high strength metallic glasses, the cells are formed in short time due to the release of high amount of stored elastic energy. In this case the uniform cell morphology with the cell size of about 20 nm is observed.
Originele taal-2English
Pagina's (van-tot)212-216
Aantal pagina's5
TijdschriftDefect and Diffusion Forum
Volume405
DOI's
StatusPublished - nov-2020

Citeer dit